prEN ISO 14720-2
Testing of ceramic materials - Determination of sulfur in non-oxidic ceramic raw materials and ceramic materials - Part 2: Inductively coupled plasma optical emission spectrometry (ICP-OES) or ion chromatography (IC) after burning in the oxygen flow (ISO/DIS 14720-2:2025)
Draft Public enquiryProject stage codes
1. Prioritetinių darbo temų pažymėjimas ir ekspertų skyrimas
2. Projektas
3. Viešoji apklausa
From 2025-03-07
till 2025-05-06
4. Closure of enquiry
5. Submission to Formal Vote
Organisation
CEN Europos standartizacijos komitetasICS
81.060.10 - Raw materialsTechnical Committee
TK 58 Refractory products and materials (dormant)ForeignTC'S
CEN/TC 187Number of comments
0Comment start date
2025-03-07Scope
This part of ISO 14720 defines a method for the determination of sulfur in powdered and granular non-oxidic ceramic raw materials and materials, which are completely oxidized at a higher temperature in an oxygen atmosphere, e.g. carbon and graphite materials. For materials which are not completely oxidizable under these conditions, it is possible to determine sulfur that can be released under these conditions, e.g. the adherent sulfur. This part of ISO 14720 is applicable for materials with mass fractions of sulfur ≤ 10 % and mass fractions of ash < 20 %, The defined method is limited for materials with mass fractions of barium < 10 mg/kg, because the sulfur bonded in barium sulfate is not detectable with this method. For the lower detection limit of this method, a mass fraction of sulfur of 0,5 mg/kg in the case of inductively coupled plasma optical emission spectrometry (ICP/OES) and 5 mg/kg in the case of ion chromatography (IC) has to be considered as a recommended value.Relations