prEN ISO 1628-5 Naujas

Komentavimo iki data 2026-08-25

Plastikai. Praskiesto polimerų tirpalo klampos nustatymas kapiliariniais viskozimetrais. 5 dalis. Termoplastinių poliesterių (TP) homopolimerai ir kopolimerai (ISO/DIS 1628-5:2026)

This part of ISO 1628 specifies a method for the determination of the viscosity number (also referred to as "reduced viscosity") of dilute solutions of thermoplastic polyesters (TPs) in certain specified solvents. The method is applicable to poly(ethylene terephthalate) (PET), poly(butylene terephthalate) (PBT), poly-(cyclohexylenedimethylene terephthalate) (PCT), and poly(ethylene naphthalate) (PEN), as well as to copolyesters and other polyesters, referred to in ISO 20028-1:2019, that are soluble in one of the specified solvents under the specified conditions. The viscosity number is determined by the general procedure specified in ISO 1628-1:2024, observing the particular conditions specified in this part of ISO 1628. The determination of the viscosity number of a thermoplastic polyester provides a measure of the relative molecular mass of the polymer.

Peržiūrėti metaduomenis

prEN ISO 1628-2 Naujas

Komentavimo iki data 2026-08-25

Plastikai. Praskiestų polimerų tirpalų klampos nustatymas kapiliariniais viskozimetrais. 2 dalis. Polivinilchloridinės dervos (ISO/DIS 1628-2:2026)

1.1 This document specifies conditions for the determination of the reduced viscosity (also known as viscosity number) and K-value of PVC resins. It is applicable to resins in powder form which consist of homopolymers of the monomer vinyl chloride and copolymers, terpolymers, etc., of vinyl chloride with one or more other monomers, but where vinyl chloride is the main constituent. The resins can contain small amounts of unpolymerized substances (e.g. emulsifying or suspending agents, catalyst residues, etc.) and other substances added during the course of the polymerization. This document is not applicable, however, to resins having a volatile-matter content in excess of 0,5 % ± 0,1 %, when determined in accordance with ISO 1269:2006. In addition to this, it is not applicable to resins which are not entirely soluble in cyclohexanone. 1.2 The reduced viscosity and K-value of a particular resin are related to its molecular mass, but the relationship varies depending on the concentration and type(s) of other monomer(s) present. Hence, homopolymers and copolymers having the same reduced viscosity or K-value can have different molecular masses. 1.3 The values determined for reduced viscosity and K-value, for a particular sample of PVC resin, are influenced differently by the concentration of the solution chosen for the determination. Hence the use of the procedures specified in this document only gives values for reduced viscosity and K-value that are comparable when the concentrations of the solutions used are identical. 1.4 The experimental procedures specified in this document can also be used to characterize the polymeric fraction obtained during the chemical analysis of a PVC composition. However, the values calculated for the reduced viscosity and K-value in these circumstances can deviate form the correct values for the resin used to produce the composition because of the impure nature of the recovered polymer fraction.

Peržiūrėti metaduomenis

prEN ISO 1628-3 Naujas

Komentavimo iki data 2026-08-25

Plastikai. Praskiestų polimerų tirpalų klampos nustatymas kapiliariniais viskozimetrais. 3 dalis. Polietilenai ir polipropilenai (ISO/DIS 1628-3:2026)

This part of ISO 1628 defines particular conditions for determining the reduced viscosity (also known as viscosity number) and intrinsic viscosity of polyethylenes and polypropylenes at elevated temperatures (135 °C – 160 °C) in dilute solution. The viscosity of polymer solutions can be affected by fillers or additives present in the sample. The value of a reduced viscosity determined by this method can therefore be unreliable if the sample contains fillers or other additives. NOTE Reduced viscosity is also known as the Staudinger function ( Jv) and intrinsic viscosity as the Staudinger index ( Jg).

Peržiūrėti metaduomenis

prEN ISO 307 Viešoji apklausa

Komentavimo iki data 2026-08-18

Plastikai. Poliamidai. Klampos skaičiaus nustatymas (ISO/DIS 307:2026)

This document specifies a method for the determination of the viscosity number of dilute solutions of polyamides in certain specified solvents. The method is applicable to the polyamides designated PA 46, PA 6, PA 66, PA 69, PA 610, PA 612, PA 11, PA 12, PA 6T/66, PA 6I/6T, PA 6T/6I/66, PA 6T/6I, PA 6I/6T/66 and PA MXD6 as defined in ISO 16396-1, as well as to co-polyamides, compounds of polyamides and other polyamides that are soluble in one of the specified solvents under the specified conditions. The method is not applicable to polyamides produced by anionic polymerization of lactams or produced with cross-linking agents; such polyamides are normally insoluble in the specified solvents. The viscosity number is determined by the general procedure specified in ISO 1628-1:2024, observing the particular conditions specified in this document.

Skaityti, komentuoti projektą Peržiūrėti metaduomenis

Būtini slapukai

Statistikos slapukai

El. pašto prenumerata

Išplėstinė paieška

Rezultatai

Greitieji filtrai

Organizacija

Technikos komitetas

ICS